Synthetic Diamond dies (Mono Diamond Dies) are used for tube wires and wires, their durability, hardness is the best choice for the special requests of die tools.
IW Synthetic diamond dies (Mono Diamond Dies) are well widely used on special requests and the ways to solve critical cost control with your productions lines.
IW Synthetic diamond dies (Mono Diamond Dies) Hole Sizes:
From 0.0008inch to 0.0800inch
Or from 0.0200mm to 2.0000mm
IW Synthetic diamond dies (Mono Diamond Dies) Description:
Typical Reduction Angles And Bearing Length
Single crystal diamond having high hardness, good wear resistance characteristics, of such a wire drawing die surface finish is very high, but due to the anisotropic structure, leading to its hardness was anisotropic, so that the wear of the die orifice is not uniform, products are not round, coupled with scarce resources, the price is expensive, generally used as a surface high quality requirements of the finished thread pull mode or pull mode.
Single-crystal diamond Drawing core is divided into two types: natural and artificial diamond Drawing core single-crystal diamond Drawing core.
With graphite materials and alloy catalyst agent (Ni-Cr-Fe, Ni-Fe-Mn, Ni C0, Ni-Cr, Ni-Mn) at a pressure above the conditions of high temperature (13000C), high pressure (5000 MPa), re diamond crystal growth, said artificial diamond.
Single crystal multi-use hydrostatic catalyst synthesis method (also blasting method).
High pressure through a hydraulic machine, such as a cubic press while applying pressure from six directions perpendicular to the sample in the center of the cube; temperature is AC or DC generated by heating the graphite sample.
High intensity artificial diamond, in order for making impregnated diamond drill bits, drilling hard formation; impregnated diamond higher strength before making a hard and hard rocks with drills. |